Copper Alloy C85200-M01 vs C85200-M02
Copper Alloy · C85200 temper comparison
C85200-M01 and C85200-M02 are two conditions of the same copper alloy grade, C85200: M01 (as sand cast) versus M02 (as centrifugally cast). The chemistry is identical, so every difference below comes from the condition. C85200-M02 is the stronger of the two: yield strength 103 MPa (14.9 ksi) against 90 MPa (13.1 ksi) for C85200-M01, about 14% more; tensile strength follows at 283 MPa (41 ksi) vs 262 MPa (38 ksi). In exchange, C85200-M01 is the more ductile: elongation 35% versus 30% for C85200-M02, and C85200-M02 is harder (50 HB vs 45 HB).
C85200-M01Choose it when the part is bent, formed or impact-loaded.
C85200-M02Choose it when strength drives the design.
C85200-M01 vs C85200-M02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 90 GPa13.1 Msi · Shear Modulus 34 GPa4.9 Msi · Bulk Modulus 105 GPa15.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 925°C1,697 °F · Liquidus Temperature 940°C1,724 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 84 W/m·K48.5 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.3 µm/m·K11.3 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 22 % IACS · Electrical Resistivity 7.8×10⁻⁸ Ω·m3.07 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 55 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 80 / 100 · Machinability Rating (AISI 1212 = 100 %) 80% · Weldability 20 / 100 · Formability (cold) 15 / 100 · Castability 85 / 100 · Brazeability / Solderability 90 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 42 MJ/kg18,057 BTU/lb · Embodied Carbon (primary production) 3 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 90%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C85200-M01 vs C85200-M02 — frequently asked
Is C85200-M02 stronger than C85200-M01?
Yes. C85200-M02 has a typical yield strength of 103 MPa (14.9 ksi) against 90 MPa (13.1 ksi) for C85200-M01 — about 14% more. Tensile strength is 283 MPa (41 ksi) vs 262 MPa (38 ksi).
Which condition does FabDigit quote by default, M01 or M02?
M01 is the default C85200 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C85200-M01 over C85200-M02?
Pick C85200-M01 when the part is bent, formed or impact-loaded. Pick C85200-M02 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C85200-M01 and C85200-M02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.