Copper Alloy C83600-M02 vs C83600-M06
Copper Alloy · C83600 temper comparison
C83600-M02 and C83600-M06 are two conditions of the same copper alloy grade, C83600: M02 (as centrifugally cast) versus M06 (as investment cast). The chemistry is identical, so every difference below comes from the condition. C83600-M02 is the stronger of the two: yield strength 124 MPa (18 ksi) against 110 MPa (16 ksi) for C83600-M06, about 13% more; tensile strength follows at 262 MPa (38 ksi) vs 241 MPa (35 ksi). C83600-M02 is the more ductile: elongation 28% versus 25% for C83600-M06, and C83600-M02 is harder (62 HB vs 58 HB).
C83600-M02Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
C83600-M02 vs C83600-M06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 83 GPa12 Msi · Shear Modulus 31 GPa4.5 Msi · Bulk Modulus 100 GPa14.5 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.83 g/cm³0.32 lb/in³ · Melting Point (Solidus) 854°C1,569 °F · Liquidus Temperature 1,010°C1,850 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 72 W/m·K41.6 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18 µm/m·K10 µin/in·°F · Latent Heat of Fusion 185 J/g79.5 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -100°C-148 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 15 % IACS · Electrical Resistivity 1.15×10⁻⁷ Ω·m4.53 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Same in both: Machinability 84 / 100 · Machinability Rating (AISI 1212 = 100 %) 210% · Weldability 20 / 100 · Castability 92 / 100 · Brazeability / Solderability 82 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 50 MJ/kg21,496 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 280 L/kg33.6 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C83600-M02 vs C83600-M06 — frequently asked
Is C83600-M02 stronger than C83600-M06?
Yes. C83600-M02 has a typical yield strength of 124 MPa (18 ksi) against 110 MPa (16 ksi) for C83600-M06 — about 13% more. Tensile strength is 262 MPa (38 ksi) vs 241 MPa (35 ksi).
Which condition does FabDigit quote by default, M02 or M06?
M01 is the default C83600 condition in the FabDigit quote flow (neither M02 nor M06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C83600-M02 over C83600-M06?
Pick C83600-M02 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C83600-M02 and C83600-M06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.