Copper Alloy C72150-H02 vs C72150-HR
Copper Alloy · C72150 temper comparison
C72150-H02 and C72150-HR are two conditions of the same copper alloy grade, C72150: H02 (half hard) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. C72150-H02 is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 280 MPa (40.6 ksi) for C72150-HR, about 71% more; tensile strength follows at 620 MPa (89.9 ksi) vs 500 MPa (72.5 ksi). In exchange, C72150-HR is the more ductile: elongation 28% versus 12% for C72150-H02, and C72150-H02 is harder (171 HB vs 124 HB). C72150-HR runs hotter in service (500°C vs 250°C continuous).
C72150-H02Choose it when strength drives the design.
C72150-HRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C72150-H02 vs C72150-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 61 GPa8.8 Msi · Bulk Modulus 158 GPa22.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.9 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,280°C2,336 °F · Liquidus Temperature 1,300°C2,372 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 21.5 W/m·K12.4 BTU/hr·ft·°F · Specific Heat Capacity 410 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 14.9 µm/m·K8.3 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 3.5 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.18 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 45 / 100 · Brazeability / Solderability 75 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 115 MJ/kg49,441 BTU/lb · Embodied Carbon (primary production) 8 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C72150-H02 vs C72150-HR — frequently asked
Is C72150-H02 stronger than C72150-HR?
Yes. C72150-H02 has a typical yield strength of 480 MPa (69.6 ksi) against 280 MPa (40.6 ksi) for C72150-HR — about 71% more. Tensile strength is 620 MPa (89.9 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, H02 or HR?
O60 is the default C72150 condition in the FabDigit quote flow (neither H02 nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C72150-H02 or C72150-HR?
C72150-H02, by a small margin. Both rate poor for machinability — 28/100 against 22/100 for C72150-HR; for welding the order is C72150-HR first (good, 60/100) then C72150-H02 (good, 55/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C72150-H02 and C72150-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.