Copper Alloy C69710-H02 vs C69710-O61
Copper Alloy · C69710 temper comparison
C69710-H02 and C69710-O61 are two conditions of the same copper alloy grade, C69710: H02 (half hard) versus O61 (annealed). The chemistry is identical, so every difference below comes from the condition. C69710-H02 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 170 MPa (24.7 ksi) for C69710-O61, about 124% more; tensile strength follows at 550 MPa (79.8 ksi) vs 400 MPa (58 ksi). In exchange, C69710-O61 is the more ductile: elongation 35% versus 12% for C69710-H02, and C69710-H02 is harder (160 HB vs 95 HB). On the shop floor, C69710-H02 machines more easily (excellent vs very good).
C69710-H02Choose it when strength drives the design, or when the part is machined in volume.
C69710-O61Choose it when the part is bent, formed or impact-loaded.
C69710-H02 vs C69710-O61: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.3 g/cm³0.3 lb/in³ · Melting Point (Solidus) 821°C1,510 °F · Liquidus Temperature 916°C1,681 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 30 W/m·K17.3 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.2 µm/m·K11.2 µin/in·°F · Latent Heat of Fusion 175 J/g75.2 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 35 / 100 · Brazeability / Solderability 75 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C69710-H02 vs C69710-O61 — frequently asked
Is C69710-H02 stronger than C69710-O61?
Yes. C69710-H02 has a typical yield strength of 380 MPa (55.1 ksi) against 170 MPa (24.7 ksi) for C69710-O61 — about 124% more. Tensile strength is 550 MPa (79.8 ksi) vs 400 MPa (58 ksi).
Which condition does FabDigit quote by default, H02 or O61?
M30 is the default C69710 condition in the FabDigit quote flow (neither H02 nor O61). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C69710-H02 or C69710-O61?
C69710-H02. Its machinability rates excellent (85/100) against very good (70/100) for C69710-O61.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C69710-H02 and C69710-O61 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.