Copper Alloy C64700-TD02 vs C64700-TH01
Copper Alloy · C64700 temper comparison
C64700-TD02 and C64700-TH01 are two conditions of the same copper alloy grade, C64700: TD02 (solution heat treated and cold worked, half hard) versus TH01 (TD01 and precipitation hardened). The chemistry is identical, so every difference below comes from the condition. C64700-TH01 is the stronger of the two: yield strength 515 MPa (74.7 ksi) against 380 MPa (55.1 ksi) for C64700-TD02, about 36% more; tensile strength follows at 600 MPa (87 ksi) vs 460 MPa (66.7 ksi). C64700-TH01 is harder — 180 HB against 135 HB for C64700-TD02 — which matters for wear surfaces and threads. C64700-TH01 runs hotter in service (200°C vs 150°C continuous) and C64700-TH01 conducts heat better (158 W/m·K vs 115 W/m·K). On the shop floor, C64700-TD02 forms better (good vs poor).
C64700-TH01Choose it when strength drives the design, or when surface hardness matters.
C64700-TD02 vs C64700-TH01: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 132 GPa19.1 Msi · Shear Modulus 49 GPa7.1 Msi · Bulk Modulus 130 GPa18.9 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.83 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,030°C1,886 °F · Liquidus Temperature 1,090°C1,994 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 75 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 62 MJ/kg26,655 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C64700-TD02 vs C64700-TH01 — frequently asked
Is C64700-TH01 stronger than C64700-TD02?
Yes. C64700-TH01 has a typical yield strength of 515 MPa (74.7 ksi) against 380 MPa (55.1 ksi) for C64700-TD02 — about 36% more. Tensile strength is 600 MPa (87 ksi) vs 460 MPa (66.7 ksi).
Which condition does FabDigit quote by default, TD02 or TH01?
TF00 is the default C64700 condition in the FabDigit quote flow (neither TD02 nor TH01). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C64700-TD02 or C64700-TH01?
C64700-TH01, by a small margin. Both rate fair for machinability — 45/100 against 36/100 for C64700-TD02; for welding the order is C64700-TH01 first (very good, 70/100) then C64700-TD02 (good, 65/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C64700-TD02 and C64700-TH01 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.