Copper Alloy C52100-H02 vs C52100-H04
Copper Alloy · C52100 temper comparison
C52100-H02 and C52100-H04 are two conditions of the same copper alloy grade, C52100: H02 (half hard) versus H04 (full hard). The chemistry is identical, so every difference below comes from the condition. C52100-H04 is the stronger of the two: yield strength 585 MPa (84.8 ksi) against 450 MPa (65.3 ksi) for C52100-H02, about 30% more; tensile strength follows at 660 MPa (95.7 ksi) vs 565 MPa (81.9 ksi). In exchange, C52100-H02 is the more ductile: elongation 28% versus 10% for C52100-H04, and C52100-H04 is harder (170 HB vs 147 HB).
C52100-H02Choose it when the part is bent, formed or impact-loaded.
C52100-H04Choose it when strength drives the design.
C52100-H02 vs C52100-H04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 110 GPa16 Msi · Shear Modulus 41 GPa5.9 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.8 g/cm³0.32 lb/in³ · Melting Point (Solidus) 854°C1,569 °F · Liquidus Temperature 1,000°C1,832 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 62 W/m·K35.8 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 18.4 µm/m·K10.2 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 13 % IACS · Electrical Resistivity 1.33×10⁻⁷ Ω·m5.24 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Same in both: Machinability 30 / 100 · Machinability Rating (AISI 1212 = 100 %) 20% · Brazeability / Solderability 88 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 72 MJ/kg30,954 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 350 L/kg41.9 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C52100-H02 vs C52100-H04 — frequently asked
Is C52100-H04 stronger than C52100-H02?
Yes. C52100-H04 has a typical yield strength of 585 MPa (84.8 ksi) against 450 MPa (65.3 ksi) for C52100-H02 — about 30% more. Tensile strength is 660 MPa (95.7 ksi) vs 565 MPa (81.9 ksi).
Which condition does FabDigit quote by default, H02 or H04?
H04 is the default C52100 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C52100-H02 over C52100-H04?
Pick C52100-H02 when the part is bent, formed or impact-loaded. Pick C52100-H04 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C52100-H02 and C52100-H04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.