Copper Alloy C36800-H01 vs C36800-M30
Copper Alloy · C36800 temper comparison
C36800-H01 and C36800-M30 are two conditions of the same copper alloy grade, C36800: H01 (quarter hard) versus M30 (as hot extruded). The chemistry is identical, so every difference below comes from the condition. C36800-H01 is the stronger of the two: yield strength 250 MPa (36.3 ksi) against 160 MPa (23.2 ksi) for C36800-M30, about 56% more; tensile strength follows at 420 MPa (60.9 ksi) vs 380 MPa (55.1 ksi). In exchange, C36800-M30 is the more ductile: elongation 40% versus 25% for C36800-H01, and C36800-H01 is harder (125 HB vs 105 HB). C36800-M30 runs hotter in service (200°C vs 180°C continuous).
C36800-H01Choose it when strength drives the design.
C36800-M30Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C36800-H01 vs C36800-M30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 112 GPa16.2 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.41 g/cm³0.3 lb/in³ · Melting Point (Solidus) 885°C1,625 °F · Liquidus Temperature 900°C1,652 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 123 W/m·K71.1 BTU/hr·ft·°F · Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.8 µm/m·K11.6 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 25 / 100 · Brazeability / Solderability 80 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C36800-H01 vs C36800-M30 — frequently asked
Is C36800-H01 stronger than C36800-M30?
Yes. C36800-H01 has a typical yield strength of 250 MPa (36.3 ksi) against 160 MPa (23.2 ksi) for C36800-M30 — about 56% more. Tensile strength is 420 MPa (60.9 ksi) vs 380 MPa (55.1 ksi).
Which condition does FabDigit quote by default, H01 or M30?
M20 is the default C36800 condition in the FabDigit quote flow (neither H01 nor M30). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C36800-H01 or C36800-M30?
C36800-H01. Its machinability rates very good (73/100) against good (68/100) for C36800-M30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C36800-H01 and C36800-M30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.