Copper Alloy C33500-H02 vs C33500-O60
Copper Alloy · C33500 temper comparison
C33500-H02 and C33500-O60 are two conditions of the same copper alloy grade, C33500: H02 (half hard) versus O60 (soft annealed). The chemistry is identical, so every difference below comes from the condition. C33500-H02 is the stronger of the two: yield strength 345 MPa (50 ksi) against 105 MPa (15.2 ksi) for C33500-O60, about 3.3 times as much; tensile strength follows at 420 MPa (60.9 ksi) vs 315 MPa (45.7 ksi). In exchange, C33500-O60 is the more ductile: elongation 65% versus 23% for C33500-H02, and C33500-H02 is harder (120 HB vs 58 HB). C33500-O60 runs hotter in service (200°C vs 180°C continuous). On the shop floor, C33500-H02 machines more easily (good vs fair).
C33500-H02Choose it when strength drives the design, or when the part is machined in volume.
C33500-O60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C33500-H02 vs C33500-O60: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 97 GPa14.1 Msi · Shear Modulus 37 GPa5.4 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 900°C1,652 °F · Liquidus Temperature 930°C1,706 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 115 W/m·K66.4 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.3 µm/m·K11.3 µin/in·°F · Latent Heat of Fusion 160 J/g68.8 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.26 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 22 / 100 · Brazeability / Solderability 80 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 65%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C33500-H02 vs C33500-O60 — frequently asked
Is C33500-H02 stronger than C33500-O60?
Yes. C33500-H02 has a typical yield strength of 345 MPa (50 ksi) against 105 MPa (15.2 ksi) for C33500-O60 — about 3.3 times as much. Tensile strength is 420 MPa (60.9 ksi) vs 315 MPa (45.7 ksi).
Which condition does FabDigit quote by default, H02 or O60?
H02 is the default C33500 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C33500-H02 or C33500-O60?
C33500-H02. Its machinability rates good (58/100) against fair (45/100) for C33500-O60.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C33500-H02 and C33500-O60 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.