Copper Alloy C27000-H02 vs C27000-H08
Copper Alloy · C27000 temper comparison
C27000-H02 and C27000-H08 are two conditions of the same copper alloy grade, C27000: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C27000-H08 is the stronger of the two: yield strength 470 MPa (68.2 ksi) against 340 MPa (49.3 ksi) for C27000-H02, about 38% more; tensile strength follows at 620 MPa (89.9 ksi) vs 430 MPa (62.4 ksi). In exchange, C27000-H02 is the more ductile: elongation 23% versus 4% for C27000-H08, and C27000-H08 is harder (180 HB vs 125 HB). C27000-H02 runs hotter in service (150°C vs 100°C continuous).
C27000-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C27000-H08Choose it when strength drives the design.
C27000-H02 vs C27000-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 105 GPa15.2 Msi · Shear Modulus 39 GPa5.7 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.47 g/cm³0.31 lb/in³ · Melting Point (Solidus) 905°C1,661 °F · Liquidus Temperature 932°C1,710 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 121 W/m·K69.9 BTU/hr·ft·°F · Specific Heat Capacity 375 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 20.3 µm/m·K11.3 µin/in·°F · Latent Heat of Fusion 170 J/g73.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 6.4×10⁻⁸ Ω·m2.52 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.27 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 40 / 100 · Castability 55 / 100 · Brazeability / Solderability 90 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 50%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C27000-H02 vs C27000-H08 — frequently asked
Is C27000-H08 stronger than C27000-H02?
Yes. C27000-H08 has a typical yield strength of 470 MPa (68.2 ksi) against 340 MPa (49.3 ksi) for C27000-H02 — about 38% more. Tensile strength is 620 MPa (89.9 ksi) vs 430 MPa (62.4 ksi).
Which condition does FabDigit quote by default, H02 or H08?
H02 is the default C27000 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C27000-H02 or C27000-H08?
C27000-H08, by a small margin. Both rate fair for machinability — 42/100 against 35/100 for C27000-H02.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C27000-H02 and C27000-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.