Copper Alloy C23400-H02 vs C23400-H08
Copper Alloy · C23400 temper comparison
C23400-H02 and C23400-H08 are two conditions of the same copper alloy grade, C23400: H02 (half hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C23400-H08 is the stronger of the two: yield strength 465 MPa (67.4 ksi) against 285 MPa (41.3 ksi) for C23400-H02, about 63% more; tensile strength follows at 525 MPa (76.1 ksi) vs 355 MPa (51.5 ksi). In exchange, C23400-H02 is the more ductile: elongation 14% versus 3% for C23400-H08, and C23400-H08 is harder (155 HB vs 105 HB). C23400-H02 runs hotter in service (200°C vs 130°C continuous).
C23400-H02Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C23400-H08Choose it when strength drives the design.
C23400-H02 vs C23400-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 112 GPa16.2 Msi · Shear Modulus 42 GPa6.1 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.34 · Reduction in Area 55%
Physical
Density and transition temperatures.
Same in both: Density 8.72 g/cm³0.32 lb/in³ · Melting Point (Solidus) 990°C1,814 °F · Liquidus Temperature 1,015°C1,859 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 150 W/m·K86.7 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.1 µm/m·K10.6 µin/in·°F · Latent Heat of Fusion 190 J/g81.7 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 34 % IACS · Electrical Resistivity 5.07×10⁻⁸ Ω·m2 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.29 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 45 / 100 · Brazeability / Solderability 95 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.5 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 40%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C23400-H02 vs C23400-H08 — frequently asked
Is C23400-H08 stronger than C23400-H02?
Yes. C23400-H08 has a typical yield strength of 465 MPa (67.4 ksi) against 285 MPa (41.3 ksi) for C23400-H02 — about 63% more. Tensile strength is 525 MPa (76.1 ksi) vs 355 MPa (51.5 ksi).
Which condition does FabDigit quote by default, H02 or H08?
H02 is the default C23400 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C23400-H02 or C23400-H08?
C23400-H08. Its machinability rates fair (37/100) against poor (32/100) for C23400-H02.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C23400-H02 and C23400-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.