Copper Alloy C18400-TB00 vs C18400-TD02
Copper Alloy · C18400 temper comparison
C18400-TB00 and C18400-TD02 are two conditions of the same copper alloy grade, C18400: TB00 (solution heat treated) versus TD02 (solution heat treated and cold worked, half hard). The chemistry is identical, so every difference below comes from the condition. C18400-TD02 is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 95 MPa (13.8 ksi) for C18400-TB00, about 3.5 times as much; tensile strength follows at 380 MPa (55.1 ksi) vs 240 MPa (34.8 ksi). In exchange, C18400-TB00 is the more ductile: elongation 40% versus 14% for C18400-TD02, and C18400-TD02 is harder (110 HB vs 60 HB). C18400-TD02 runs hotter in service (250°C vs 150°C continuous) and C18400-TD02 conducts heat better (300 W/m·K vs 190 W/m·K). On the shop floor, C18400-TD02 machines more easily (45 vs 35 out of 100).
C18400-TB00Choose it when the part is bent, formed or impact-loaded.
C18400-TD02Choose it when strength drives the design, or when the part sees heat.
C18400-TB00 vs C18400-TD02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 115 GPa16.7 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 138 GPa20 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,070°C1,958 °F · Liquidus Temperature 1,080°C1,976 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 60% · Weldability 45 / 100 · Castability 55 / 100 · Brazeability / Solderability 70 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C18400-TB00 vs C18400-TD02 — frequently asked
Is C18400-TD02 stronger than C18400-TB00?
Yes. C18400-TD02 has a typical yield strength of 330 MPa (47.9 ksi) against 95 MPa (13.8 ksi) for C18400-TB00 — about 3.5 times as much. Tensile strength is 380 MPa (55.1 ksi) vs 240 MPa (34.8 ksi).
Which condition does FabDigit quote by default, TB00 or TD02?
TF00 is the default C18400 condition in the FabDigit quote flow (neither TB00 nor TD02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C18400-TB00 or C18400-TD02?
C18400-TD02, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for C18400-TB00.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C18400-TB00 and C18400-TD02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.