Copper Alloy C16500-H06 vs C16500-H08
Copper Alloy · C16500 temper comparison
C16500-H06 and C16500-H08 are two conditions of the same copper alloy grade, C16500: H06 (extra hard) versus H08 (spring hard). The chemistry is identical, so every difference below comes from the condition. C16500-H08 is the stronger of the two: yield strength 496 MPa (71.9 ksi) against 469 MPa (68 ksi) for C16500-H06, about 6% more; tensile strength follows at 524 MPa (76 ksi) vs 496 MPa (71.9 ksi). In exchange, C16500-H06 is the more ductile: elongation 3% versus 2% for C16500-H08, and C16500-H08 is harder (140 HB vs 130 HB).
C16500-H06Choose it when the part is bent, formed or impact-loaded.
C16500-H08Choose it when strength drives the design.
C16500-H06 vs C16500-H08: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 138 GPa20 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.89 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,030°C1,886 °F · Liquidus Temperature 1,076°C1,969 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Castability 40 / 100 · Brazeability / Solderability 80 / 100 · Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.6 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C16500-H06 vs C16500-H08 — frequently asked
Is C16500-H08 stronger than C16500-H06?
Yes. C16500-H08 has a typical yield strength of 496 MPa (71.9 ksi) against 469 MPa (68 ksi) for C16500-H06 — about 6% more. Tensile strength is 524 MPa (76 ksi) vs 496 MPa (71.9 ksi).
Which condition does FabDigit quote by default, H06 or H08?
H04 is the default C16500 condition in the FabDigit quote flow (neither H06 nor H08). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, C16500-H06 or C16500-H08?
C16500-H06. Its weldability rates fair (45/100) against fair (40/100) for C16500-H08.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C16500-H06 and C16500-H08 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.