Copper Alloy C16200-H02 vs C16200-H06
Copper Alloy · C16200 temper comparison
C16200-H02 and C16200-H06 are two conditions of the same copper alloy grade, C16200: H02 (half hard) versus H06 (extra hard). The chemistry is identical, so every difference below comes from the condition. C16200-H06 is the stronger of the two: yield strength 435 MPa (63.1 ksi) against 315 MPa (45.7 ksi) for C16200-H02, about 38% more; tensile strength follows at 470 MPa (68.2 ksi) vs 370 MPa (53.7 ksi). In exchange, C16200-H02 is the more ductile: elongation 15% versus 5% for C16200-H06, and C16200-H06 is harder (125 HB vs 100 HB).
C16200-H02Choose it when the part is bent, formed or impact-loaded.
C16200-H06Choose it when strength drives the design.
C16200-H02 vs C16200-H06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,030°C1,886 °F · Liquidus Temperature 1,076°C1,969 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 85 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C16200-H02 vs C16200-H06 — frequently asked
Is C16200-H06 stronger than C16200-H02?
Yes. C16200-H06 has a typical yield strength of 435 MPa (63.1 ksi) against 315 MPa (45.7 ksi) for C16200-H02 — about 38% more. Tensile strength is 470 MPa (68.2 ksi) vs 370 MPa (53.7 ksi).
Which condition does FabDigit quote by default, H02 or H06?
H04 is the default C16200 condition in the FabDigit quote flow (neither H02 nor H06). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C16200-H02 or C16200-H06?
C16200-H06, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for C16200-H02; for welding the order is C16200-H02 first (fair, 40/100) then C16200-H06 (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C16200-H02 and C16200-H06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.