Copper Alloy C15760-H01 vs C15760-H02
Copper Alloy · C15760 temper comparison
C15760-H01 and C15760-H02 are two conditions of the same copper alloy grade, C15760: H01 (quarter hard) versus H02 (half hard). The chemistry is identical, so every difference below comes from the condition. C15760-H02 is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 440 MPa (63.8 ksi) for C15760-H01, about 11% more; tensile strength follows at 555 MPa (80.5 ksi) vs 525 MPa (76.1 ksi). In exchange, C15760-H01 is the more ductile: elongation 16% versus 14% for C15760-H02, and C15760-H02 is harder (152 HB vs 140 HB).
C15760-H01Choose it when the part is bent, formed or impact-loaded.
C15760-H02Choose it when strength drives the design.
C15760-H01 vs C15760-H02: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 130 GPa18.9 Msi · Shear Modulus 48 GPa7 Msi · Bulk Modulus 138 GPa20 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 8.81 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,083°C1,981 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 322 W/m·K186 BTU/hr·ft·°F · Specific Heat Capacity 380 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.6 µm/m·K9.2 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Max Service Temperature (continuous) 500°C932 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 78 % IACS · Electrical Resistivity 2.21×10⁻⁸ Ω·m0.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 30 / 100 · Castability 5 / 100 · Brazeability / Solderability 70 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 75 MJ/kg32,244 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 260 L/kg31.2 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C15760-H01 vs C15760-H02 — frequently asked
Is C15760-H02 stronger than C15760-H01?
Yes. C15760-H02 has a typical yield strength of 490 MPa (71.1 ksi) against 440 MPa (63.8 ksi) for C15760-H01 — about 11% more. Tensile strength is 555 MPa (80.5 ksi) vs 525 MPa (76.1 ksi).
Which condition does FabDigit quote by default, H01 or H02?
H04 is the default C15760 condition in the FabDigit quote flow (neither H01 nor H02). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C15760-H01 over C15760-H02?
Pick C15760-H01 when the part is bent, formed or impact-loaded. Pick C15760-H02 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C15760-H01 and C15760-H02 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.