Copper Alloy C14200-H04 vs C14200-O61
Copper Alloy · C14200 temper comparison
C14200-H04 and C14200-O61 are two conditions of the same copper alloy grade, C14200: H04 (full hard) versus O61 (annealed). The chemistry is identical, so every difference below comes from the condition. C14200-H04 is the stronger of the two: yield strength 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for C14200-O61, about 4.4 times as much; tensile strength follows at 350 MPa (50.8 ksi) vs 225 MPa (32.6 ksi). In exchange, C14200-O61 is the more ductile: elongation 45% versus 6% for C14200-H04, and C14200-H04 is harder (95 HB vs 42 HB). C14200-O61 runs hotter in service (300°C vs 200°C continuous).
C14200-H04Choose it when strength drives the design.
C14200-O61Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C14200-H04 vs C14200-O61: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 190 W/m·K110 BTU/hr·ft·°F · Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.7 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 4.3×10⁻⁸ Ω·m1.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.2 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 30 / 100 · Weldability 70 / 100 · Brazeability / Solderability 95 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 58 MJ/kg24,936 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C14200-H04 vs C14200-O61 — frequently asked
Is C14200-H04 stronger than C14200-O61?
Yes. C14200-H04 has a typical yield strength of 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for C14200-O61 — about 4.4 times as much. Tensile strength is 350 MPa (50.8 ksi) vs 225 MPa (32.6 ksi).
Which condition does FabDigit quote by default, H04 or O61?
OS050 is the default C14200 condition in the FabDigit quote flow (neither H04 nor O61). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C14200-H04 over C14200-O61?
Pick C14200-H04 when strength drives the design. Pick C14200-O61 when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C14200-H04 and C14200-O61 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.