Copper Alloy C1220 1/2H vs C1220-H
Copper Alloy · C1220 temper comparison
C1220 1/2H and C1220-H are two conditions of the same copper alloy grade, C1220: 1/2H (half hard) versus H (hardened). The chemistry is identical, so every difference below comes from the condition. C1220-H is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 250 MPa (36.3 ksi) for C1220 1/2H, about 20% more; tensile strength follows at 345 MPa (50 ksi) vs 305 MPa (44.2 ksi). In exchange, C1220 1/2H is the more ductile: elongation 15% versus 10% for C1220-H, and C1220-H is harder (110 HV vs 95 HV). C1220 1/2H runs hotter in service (200°C vs 150°C continuous).
C1220 1/2HChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
C1220-HChoose it when strength drives the design.
C1220 1/2H vs C1220-H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Reduction in Area 75% · Charpy V-Notch Impact (RT) 60 J44.3 ft·lbf · Hardness, Brinell 45 HB
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.6 µm/m·K9.8 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 84 % IACS · Electrical Resistivity 2.03×10⁻⁸ Ω·m0.799 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 25 / 100 · Weldability 80 / 100 · Castability 40 / 100 · Brazeability / Solderability 100 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C1220 1/2H vs C1220-H — frequently asked
Is C1220-H stronger than C1220 1/2H?
Yes. C1220-H has a typical yield strength of 300 MPa (43.5 ksi) against 250 MPa (36.3 ksi) for C1220 1/2H — about 20% more. Tensile strength is 345 MPa (50 ksi) vs 305 MPa (44.2 ksi).
Which condition does FabDigit quote by default, 1/2H or H?
O is the default C1220 condition in the FabDigit quote flow (neither 1/2H nor H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C1220 1/2H over C1220-H?
Pick C1220 1/2H when the part is bent, formed or impact-loaded, or when the part sees heat. Pick C1220-H when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C1220 1/2H and C1220-H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.