Copper Alloy BrAZhMts10-3-1.5-ANN vs BrAZhMts10-3-1.5 CHILL
Copper Alloy · BrAZhMts10-3-1.5 temper comparison
BrAZhMts10-3-1.5-ANN and BrAZhMts10-3-1.5 CHILL are two conditions of the same copper alloy grade, BrAZhMts10-3-1.5: ANN (annealed) versus CHILL (chill / permanent-mould cast). The chemistry is identical, so every difference below comes from the condition. Both yield at about 240 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (annealed versus chill / permanent-mould cast). BrAZhMts10-3-1.5-ANN is the more ductile: elongation 20% versus 14% for BrAZhMts10-3-1.5 CHILL, and BrAZhMts10-3-1.5-ANN is harder (140 HB vs 130 HB).
BrAZhMts10-3-1.5-ANNChoose it when the part is bent, formed or impact-loaded.
BrAZhMts10-3-1.5-ANN vs BrAZhMts10-3-1.5 CHILL: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
BrAZhMts10-3-1.5-ANNBrAZhMts10-3-1.5 CHILL
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 42 GPa6.1 Msi · Bulk Modulus 115 GPa16.7 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 7.5 g/cm³0.27 lb/in³ · Melting Point (Solidus) 1,040°C1,904 °F · Liquidus Temperature 1,055°C1,931 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 59 W/m·K34.1 BTU/hr·ft·°F · Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 220 J/g94.6 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 13 % IACS · Electrical Resistivity 1.33×10⁻⁷ Ω·m5.24 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.28 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 28% · Castability 70 / 100 · Brazeability / Solderability 30 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4 kg CO₂/kg · Embodied Water 300 L/kg35.9 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
BrAZhMts10-3-1.5-ANN vs BrAZhMts10-3-1.5 CHILL — frequently asked
What is the difference between BrAZhMts10-3-1.5-ANN and BrAZhMts10-3-1.5 CHILL?
BrAZhMts10-3-1.5-ANN and BrAZhMts10-3-1.5 CHILL are two conditions of the same copper alloy grade, BrAZhMts10-3-1.5: ANN (annealed) versus CHILL (chill / permanent-mould cast). The chemistry is identical, so every difference below comes from the condition. Both yield at about 240 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (annealed versus chill / permanent-mould cast).
Which condition does FabDigit quote by default, ANN or CHILL?
SAND is the default BrAZhMts10-3-1.5 condition in the FabDigit quote flow (neither ANN nor CHILL). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, BrAZhMts10-3-1.5-ANN or BrAZhMts10-3-1.5 CHILL?
BrAZhMts10-3-1.5-ANN. Its weldability rates very good (75/100) against good (68/100) for BrAZhMts10-3-1.5 CHILL.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BrAZhMts10-3-1.5-ANN and BrAZhMts10-3-1.5 CHILL side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.