PMI Foam Core (Rohacell) 200WF vs PMI Foam Core (Rohacell) A
Composite · PMI Foam Core (Rohacell) grade comparison
PMI Foam Core (Rohacell) 200WF and PMI Foam Core (Rohacell) A are two grades of the same composite grade, PMI Foam Core (Rohacell): 200WF versus A (solution annealed). The chemistry is identical, so every difference below comes from the condition. PMI Foam Core (Rohacell) 200WF is the stronger of the two: tensile strength 7 MPa (0.986 ksi) against 2 MPa (0.29 ksi) for PMI Foam Core (Rohacell) A, about 3.4 times as much. PMI Foam Core (Rohacell) 200WF is the more ductile: elongation 4.5% versus 3% for PMI Foam Core (Rohacell) A. PMI Foam Core (Rohacell) A is lighter (0.08 g/cm³ vs 0.21 g/cm³ for PMI Foam Core (Rohacell) 200WF) and PMI Foam Core (Rohacell) 200WF is stiffer (0.35 GPa vs 0.09 GPa).
PMI Foam Core (Rohacell) 200WFChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
PMI Foam Core (Rohacell) AChoose it when weight is the constraint.
PMI Foam Core (Rohacell) 200WF vs PMI Foam Core (Rohacell) A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PMI Foam Core (Rohacell) 200WFPMI Foam Core (Rohacell) A
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Shear Strength
Same in both: Poisson's Ratio 0.3 · Compressive Modulus 0.09 GPa0.01 Msi
Physical
Density and transition temperatures.
Density
Same in both: Glass Transition (Tg) 210°C410 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 1,500 J/kg·K0.36 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 35 µm/m·K19.4 µin/in·°F · Max Service Temperature (continuous) 180°C356 °F · Min Service Temperature -196°C-321 °F · Max Service Temperature (short-term) 200°C392 °F
Electrical
Conductivity and insulation.
Same in both: Dielectric Constant (1 MHz) 1.1 · Dissipation Factor (1 MHz) 5×10⁻⁴
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: UV / Weathering Resistance 25 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 130 MJ/kg55,890 BTU/lb · Embodied Carbon (primary production) 6.5 kg CO₂/kg · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PMI Foam Core (Rohacell) 200WF vs PMI Foam Core (Rohacell) A — frequently asked
Is PMI Foam Core (Rohacell) 200WF stronger than PMI Foam Core (Rohacell) A?
Yes. PMI Foam Core (Rohacell) 200WF has a typical tensile strength of 7 MPa (0.986 ksi) against 2 MPa (0.29 ksi) for PMI Foam Core (Rohacell) A — about 3.4 times as much.
Which grade does FabDigit quote by default, 200WF or A?
71IG-F is the default PMI Foam Core (Rohacell) condition in the FabDigit quote flow (neither 200WF nor A). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PMI Foam Core (Rohacell) 200WF or PMI Foam Core (Rohacell) A?
PMI Foam Core (Rohacell) A. Its machinability rates excellent (85/100) against very good (80/100) for PMI Foam Core (Rohacell) 200WF.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PMI Foam Core (Rohacell) 200WF and PMI Foam Core (Rohacell) A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.