A359/SiC/20p T5 vs A359/SiC/20p T6
Composite · A359/SiC/20p grade comparison
A359/SiC/20p T5 and A359/SiC/20p T6 are two grades of the same composite grade, A359/SiC/20p: T5 (cooled from hot working and artificially aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. A359/SiC/20p T6 is the stronger of the two: yield strength 310 MPa (45 ksi) against 235 MPa (34.1 ksi) for A359/SiC/20p T5, about 32% more; tensile strength follows at 340 MPa (49.3 ksi) vs 275 MPa (39.9 ksi). In exchange, A359/SiC/20p T5 is the more ductile: elongation 0.6% versus 0.5% for A359/SiC/20p T6.
A359/SiC/20p T5Choose it when the part is bent, formed or impact-loaded.
A359/SiC/20p T6Choose it when strength drives the design.
A359/SiC/20p T5 vs A359/SiC/20p T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
A359/SiC/20p T5A359/SiC/20p T6
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Same in both: Elastic (Young's) Modulus 98.6 GPa14.3 Msi · Shear Modulus 38 GPa5.5 Msi · Bulk Modulus 82 GPa11.9 Msi · Poisson's Ratio 0.32 · Compressive Modulus 99 GPa14.4 Msi · Flexural Modulus 98 GPa14.2 Msi
Physical
Density and transition temperatures.
Same in both: Density 2.77 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 180 W/m·K104 BTU/hr·ft·°F · Specific Heat Capacity 840 J/kg·K0.2 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17.5 µm/m·K9.7 µin/in·°F · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -196°C-321 °F · Max Service Temperature (short-term) 300°C572 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 6×10⁻⁸ Ω·m2.36 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 45 / 100 · UV / Weathering Resistance 95 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 190 MJ/kg81,685 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A359/SiC/20p T5 vs A359/SiC/20p T6 — frequently asked
Is A359/SiC/20p T6 stronger than A359/SiC/20p T5?
Yes. A359/SiC/20p T6 has a typical yield strength of 310 MPa (45 ksi) against 235 MPa (34.1 ksi) for A359/SiC/20p T5 — about 32% more. Tensile strength is 340 MPa (49.3 ksi) vs 275 MPa (39.9 ksi).
Which grade does FabDigit quote by default, T5 or T6?
T6 is the default A359/SiC/20p condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose A359/SiC/20p T5 over A359/SiC/20p T6?
Pick A359/SiC/20p T5 when the part is bent, formed or impact-loaded. Pick A359/SiC/20p T6 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A359/SiC/20p T5 and A359/SiC/20p T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.