6092/SiC/17.5p O vs 6092/SiC/17.5p T6
Composite · 6092/SiC/17.5p grade comparison
6092/SiC/17.5p O and 6092/SiC/17.5p T6 are two grades of the same composite grade, 6092/SiC/17.5p: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6092/SiC/17.5p T6 is the stronger of the two: yield strength 434 MPa (62.9 ksi) against 150 MPa (21.8 ksi) for 6092/SiC/17.5p O, about 189% more; tensile strength follows at 483 MPa (70.1 ksi) vs 250 MPa (36.3 ksi). In exchange, 6092/SiC/17.5p O is the more ductile: elongation 12% versus 6% for 6092/SiC/17.5p T6. 6092/SiC/17.5p O runs hotter in service (200°C vs 150°C continuous).
6092/SiC/17.5p OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
6092/SiC/17.5p T6Choose it when strength drives the design.
6092/SiC/17.5p O vs 6092/SiC/17.5p T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
6092/SiC/17.5p O6092/SiC/17.5p T6
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Same in both: Shear Modulus 38.5 GPa5.6 Msi · Bulk Modulus 79 GPa11.5 Msi · Poisson's Ratio 0.29 · Compressive Modulus 102 GPa14.8 Msi
Physical
Density and transition temperatures.
Same in both: Density 2.8 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 840 J/kg·K0.2 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.4 µm/m·K9.1 µin/in·°F · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 95 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 280 MJ/kg120,378 BTU/lb · Embodied Carbon (primary production) 18 kg CO₂/kg · Embodied Water 1,300 L/kg156 gal/lb · Typical Recycled Content 2%
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6092/SiC/17.5p O vs 6092/SiC/17.5p T6 — frequently asked
Is 6092/SiC/17.5p T6 stronger than 6092/SiC/17.5p O?
Yes. 6092/SiC/17.5p T6 has a typical yield strength of 434 MPa (62.9 ksi) against 150 MPa (21.8 ksi) for 6092/SiC/17.5p O — about 189% more. Tensile strength is 483 MPa (70.1 ksi) vs 250 MPa (36.3 ksi).
Which grade does FabDigit quote by default, O or T6?
T6 is the default 6092/SiC/17.5p condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6092/SiC/17.5p O or 6092/SiC/17.5p T6?
6092/SiC/17.5p O, by a small margin. Both rate poor for machinability — 28/100 against 22/100 for 6092/SiC/17.5p T6.