5052-H39 Aluminum Honeycomb vs Cross-linked PVC Foam Core
Composite · grade comparison
5052-H39 Aluminum Honeycomb and Cross-linked PVC Foam Core are both composite grades. 5052-H39 Aluminum Honeycomb is the stronger of the two: tensile strength 3 MPa (0.406 ksi) against 3 MPa (0.363 ksi) for Cross-linked PVC Foam Core, about 12% more. 5052-H39 Aluminum Honeycomb is lighter (0.05 g/cm³ vs 0.08 g/cm³ for Cross-linked PVC Foam Core) and 5052-H39 Aluminum Honeycomb is stiffer (0.52 GPa vs 0.1 GPa). On the shop floor, Cross-linked PVC Foam Core machines more easily (excellent vs fair).
5052-H39 Aluminum HoneycombChoose it when strength drives the design, or when weight is the constraint.
Cross-linked PVC Foam CoreChoose it when the part is machined in volume.
5052-H39 Aluminum Honeycomb vs Cross-linked PVC Foam Core: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
5052-H39 Aluminum HoneycombCross-linked PVC Foam Core
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Compressive Modulus
Shear Strength
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Max Service Temperature (short-term)
Limiting Oxygen Index
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 5052-H39 Aluminum Honeycomb | Cross-linked PVC Foam Core |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
5052-H39 Aluminum Honeycomb vs Cross-linked PVC Foam Core — frequently asked
Is 5052-H39 Aluminum Honeycomb stronger than Cross-linked PVC Foam Core?
Yes. 5052-H39 Aluminum Honeycomb has a typical tensile strength of 3 MPa (0.406 ksi) against 3 MPa (0.363 ksi) for Cross-linked PVC Foam Core — about 12% more.
Which is cheaper, 5052-H39 Aluminum Honeycomb or Cross-linked PVC Foam Core?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 5052-H39 Aluminum Honeycomb or Cross-linked PVC Foam Core?
Cross-linked PVC Foam Core. Its machinability rates excellent (90/100) against fair (38/100) for 5052-H39 Aluminum Honeycomb.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5052-H39 Aluminum Honeycomb and Cross-linked PVC Foam Core side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.