Cobalt-Chrome Alloy Tribaloy T-800-AC vs Tribaloy T-800-HIP
Cobalt-Chrome Alloy · Tribaloy T-800 temper comparison
Tribaloy T-800-AC and Tribaloy T-800-HIP are two conditions of the same cobalt-chrome alloy grade, Tribaloy T-800: AC (spheroidize annealed) versus HIP (hot isostatic pressed). The chemistry is identical, so every difference below comes from the condition. Tribaloy T-800-HIP is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for Tribaloy T-800-AC, about 17% more; tensile strength follows at 600 MPa (87 ksi) vs 500 MPa (72.5 ksi). Tribaloy T-800-HIP is the more ductile: elongation 0.5% versus 0.3% for Tribaloy T-800-AC.
Tribaloy T-800-HIPChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Tribaloy T-800-AC vs Tribaloy T-800-HIP: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all cobalt-chrome alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all cobalt-chrome alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Tribaloy T-800-ACTribaloy T-800-HIP
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 87 GPa12.6 Msi · Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 8.6 g/cm³0.31 lb/in³ · Melting Point (Solidus) 1,250°C2,282 °F · Liquidus Temperature 1,320°C2,408 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 3% · Castability 60 / 100 · Brazeability / Solderability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 170 MJ/kg73,087 BTU/lb · Embodied Carbon (primary production) 16 kg CO₂/kg · Embodied Water 400 L/kg47.9 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every cobalt-chrome alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Tribaloy T-800-AC vs Tribaloy T-800-HIP — frequently asked
Is Tribaloy T-800-HIP stronger than Tribaloy T-800-AC?
Yes. Tribaloy T-800-HIP has a typical yield strength of 560 MPa (81.2 ksi) against 480 MPa (69.6 ksi) for Tribaloy T-800-AC — about 17% more. Tensile strength is 600 MPa (87 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, AC or HIP?
AC is the default Tribaloy T-800 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, Tribaloy T-800-AC or Tribaloy T-800-HIP?
Tribaloy T-800-HIP. Its weldability rates poor (25/100) against poor (20/100) for Tribaloy T-800-AC.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Tribaloy T-800-AC and Tribaloy T-800-HIP side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.