Aluminum EN AC-45400-T4 vs EN AC-45400-T6
Aluminum · EN AC-45400 temper comparison
EN AC-45400-T4 and EN AC-45400-T6 are two conditions of the same aluminum grade, EN AC-45400: T4 (solution heat treated and naturally aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. EN AC-45400-T6 is the stronger of the two: yield strength 225 MPa (32.6 ksi) against 130 MPa (18.9 ksi) for EN AC-45400-T4, about 73% more; tensile strength follows at 285 MPa (41.3 ksi) vs 250 MPa (36.3 ksi). In exchange, EN AC-45400-T4 is the more ductile: elongation 6% versus 1.5% for EN AC-45400-T6, and EN AC-45400-T6 is harder (105 HB vs 80 HB). EN AC-45400-T6 conducts electricity better (29 % IACS vs 26 % IACS).
EN AC-45400-T4Choose it when the part is bent, formed or impact-loaded.
EN AC-45400-T6Choose it when strength drives the design.
EN AC-45400-T4 vs EN AC-45400-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 75 GPa10.9 Msi · Shear Modulus 28 GPa4.1 Msi · Bulk Modulus 74 GPa10.7 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 20 MPa·√m18.2 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 2.75 g/cm³0.1 lb/in³ · Melting Point (Solidus) 525°C977 °F · Liquidus Temperature 625°C1,157 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 21.5 µm/m·K11.9 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 6.6×10⁻⁸ Ω·m2.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V · Corrosion Resistance 38 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Machinability Rating (AISI 1212 = 100 %) 70% · Weldability 30 / 100 · Formability (cold) 5 / 100 · Castability 80 / 100 · Brazeability / Solderability 20 / 100 · Polishability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 10 kg CO₂/kg · Embodied Water 1,100 L/kg132 gal/lb · Typical Recycled Content 80%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
EN AC-45400-T4 vs EN AC-45400-T6 — frequently asked
Is EN AC-45400-T6 stronger than EN AC-45400-T4?
Yes. EN AC-45400-T6 has a typical yield strength of 225 MPa (32.6 ksi) against 130 MPa (18.9 ksi) for EN AC-45400-T4 — about 73% more. Tensile strength is 285 MPa (41.3 ksi) vs 250 MPa (36.3 ksi).
Which condition does FabDigit quote by default, T4 or T6?
T4 is the default EN AC-45400 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose EN AC-45400-T4 over EN AC-45400-T6?
Pick EN AC-45400-T4 when the part is bent, formed or impact-loaded. Pick EN AC-45400-T6 when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in EN AC-45400-T4 and EN AC-45400-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.