Aluminum AC8A-F vs AC8A-T6
Aluminum · AC8A temper comparison
AC8A-F and AC8A-T6 are two conditions of the same aluminum grade, AC8A: F (as fabricated) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. AC8A-T6 is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 140 MPa (20.3 ksi) for AC8A-F, about 71% more; tensile strength follows at 285 MPa (41.3 ksi) vs 190 MPa (27.6 ksi). In exchange, AC8A-F is the more ductile: elongation 1.5% versus 1% for AC8A-T6, and AC8A-T6 is harder (115 HB vs 85 HB). AC8A-T6 runs hotter in service (250°C vs 200°C continuous).
AC8A-FChoose it when the part is bent, formed or impact-loaded.
AC8A-T6Choose it when strength drives the design, or when the part sees heat.
AC8A-F vs AC8A-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 525°C977 °F · Liquidus Temperature 580°C1,076 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 880 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 19.5 µm/m·K10.8 µin/in·°F · Latent Heat of Fusion 470 J/g202 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 85 / 100 · Brazeability / Solderability 20 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 60%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
AC8A-F vs AC8A-T6 — frequently asked
Is AC8A-T6 stronger than AC8A-F?
Yes. AC8A-T6 has a typical yield strength of 240 MPa (34.8 ksi) against 140 MPa (20.3 ksi) for AC8A-F — about 71% more. Tensile strength is 285 MPa (41.3 ksi) vs 190 MPa (27.6 ksi).
Which condition does FabDigit quote by default, F or T6?
T6 is the default AC8A condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, AC8A-F or AC8A-T6?
AC8A-F. Its machinability rates good (55/100) against fair (50/100) for AC8A-T6; for welding the order is AC8A-F first (poor, 30/100) then AC8A-T6 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in AC8A-F and AC8A-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.