Aluminum 7049-T7351 vs 7049-T7452
Aluminum · 7049 temper comparison
7049-T7351 and 7049-T7452 are two conditions of the same aluminum grade, 7049: T7351 (T73, stress relieved by stretching) versus T7452 (t74-type overage, stress-relieved by compression). The chemistry is identical, so every difference below comes from the condition. 7049-T7452 is the stronger of the two: yield strength 485 MPa (70.3 ksi) against 455 MPa (66 ksi) for 7049-T7351, about 7% more. 7049-T7452 is harder — 137 HB against 130 HB for 7049-T7351 — which matters for wear surfaces and threads.
7049-T7452Choose it when strength drives the design, or when surface hardness matters.
7049-T7351 vs 7049-T7452: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 71.7 GPa10.4 Msi · Shear Modulus 26.9 GPa3.9 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 477°C891 °F · Liquidus Temperature 635°C1,175 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 960 J/kg·K0.23 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 70% · Weldability 15 / 100 · Castability 20 / 100 · Brazeability / Solderability 10 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 215 MJ/kg92,433 BTU/lb · Embodied Carbon (primary production) 13.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
7049-T7351 vs 7049-T7452 — frequently asked
Is 7049-T7452 stronger than 7049-T7351?
Yes. 7049-T7452 has a typical yield strength of 485 MPa (70.3 ksi) against 455 MPa (66 ksi) for 7049-T7351 — about 7% more. Tensile strength is 550 MPa (79.8 ksi) vs 525 MPa (76.1 ksi).
Which condition does FabDigit quote by default, T7351 or T7452?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
When should I choose 7049-T7351 over 7049-T7452?
Pick 7049-T7452 when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 7049-T7351 and 7049-T7452 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.