Aluminum 6162-O vs 6162-T651
Aluminum · 6162 temper comparison
6162-O and 6162-T651 are two conditions of the same aluminum grade, 6162: O (annealed) versus T651 (T6, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 6162-T651 is the stronger of the two: yield strength 265 MPa (38.4 ksi) against 60 MPa (8.7 ksi) for 6162-O, about 4.4 times as much; tensile strength follows at 290 MPa (42.1 ksi) vs 125 MPa (18.1 ksi). In exchange, 6162-O is the more ductile: elongation 28% versus 11% for 6162-T651, and 6162-T651 is harder (95 HB vs 32 HB). 6162-O runs hotter in service (200°C vs 150°C continuous) and 6162-O conducts electricity better (53 % IACS vs 47 % IACS). On the shop floor, 6162-T651 machines more easily (very good vs fair).
6162-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
6162-T651Choose it when strength drives the design, or when the part is machined in volume.
6162-O vs 6162-T651: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 95 MPa13.8 ksi · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in · Hardness, Vickers 100 HV
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 615°C1,139 °F · Liquidus Temperature 655°C1,211 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 896 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 393 J/g169 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 3.67×10⁻⁸ Ω·m1.44 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V · Corrosion Resistance 68 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 190% · Weldability 80 / 100 · Castability 30 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 210 MJ/kg90,284 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6162-O vs 6162-T651 — frequently asked
Is 6162-T651 stronger than 6162-O?
Yes. 6162-T651 has a typical yield strength of 265 MPa (38.4 ksi) against 60 MPa (8.7 ksi) for 6162-O — about 4.4 times as much. Tensile strength is 290 MPa (42.1 ksi) vs 125 MPa (18.1 ksi).
Which condition does FabDigit quote by default, O or T651?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 6162-O or 6162-T651?
6162-T651. Its machinability rates very good (70/100) against fair (40/100) for 6162-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6162-O and 6162-T651 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.