Aluminum 6105-T1 vs 6105-T6
Aluminum · 6105 temper comparison
6105-T1 and 6105-T6 are two conditions of the same aluminum grade, 6105: T1 (cooled from hot working and naturally aged) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6105-T6 is the stronger of the two: yield strength 255 MPa (37 ksi) against 97 MPa (14.1 ksi) for 6105-T1, about 163% more; tensile strength follows at 290 MPa (42.1 ksi) vs 152 MPa (22 ksi). In exchange, 6105-T1 is the more ductile: elongation 16% versus 10% for 6105-T6, and 6105-T6 is harder (85 HB vs 47 HB). 6105-T6 runs hotter in service (150°C vs 120°C continuous). On the shop floor, 6105-T6 machines more easily (good vs fair).
6105-T1Choose it when the part is bent, formed or impact-loaded.
6105-T6Choose it when strength drives the design, or when the part sees heat.
6105-T1 vs 6105-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 68 GPa9.9 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 2.69 g/cm³0.1 lb/in³ · Melting Point (Solidus) 615°C1,139 °F · Liquidus Temperature 654°C1,209 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 172 W/m·K99.4 BTU/hr·ft·°F · Specific Heat Capacity 895 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6105-T1 vs 6105-T6 — frequently asked
Is 6105-T6 stronger than 6105-T1?
Yes. 6105-T6 has a typical yield strength of 255 MPa (37 ksi) against 97 MPa (14.1 ksi) for 6105-T1 — about 163% more. Tensile strength is 290 MPa (42.1 ksi) vs 152 MPa (22 ksi).
Which condition does FabDigit quote by default, T1 or T6?
T5 is the default 6105 condition in the FabDigit quote flow (neither T1 nor T6). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6105-T1 or 6105-T6?
6105-T6. Its machinability rates good (58/100) against fair (45/100) for 6105-T1.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6105-T1 and 6105-T6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.