Aluminum 6081-O vs 6081-T6
Aluminum · 6081 temper comparison
6081-O and 6081-T6 are two conditions of the same aluminum grade, 6081: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6081-T6 is the stronger of the two: yield strength 275 MPa (39.9 ksi) against 65 MPa (9.43 ksi) for 6081-O, about 4.2 times as much; tensile strength follows at 310 MPa (45 ksi) vs 130 MPa (18.9 ksi). In exchange, 6081-O is the more ductile: elongation 24% versus 11% for 6081-T6, and 6081-T6 is harder (95 HB vs 30 HB). 6081-O runs hotter in service (200°C vs 150°C continuous) and 6081-O conducts electricity better (50 % IACS vs 42 % IACS). On the shop floor, 6081-T6 machines more easily (good vs fair).
6081-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
6081-T6Choose it when strength drives the design, or when the part is machined in volume.
6081-O vs 6081-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Compressive Strength 275 MPa39.9 ksi · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 585°C1,085 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 395 J/g170 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.83 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 150% · Castability 35 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6081-O vs 6081-T6 — frequently asked
Is 6081-T6 stronger than 6081-O?
Yes. 6081-T6 has a typical yield strength of 275 MPa (39.9 ksi) against 65 MPa (9.43 ksi) for 6081-O — about 4.2 times as much. Tensile strength is 310 MPa (45 ksi) vs 130 MPa (18.9 ksi).
Which condition does FabDigit quote by default, O or T6?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 6081-O or 6081-T6?
6081-T6. Its machinability rates good (60/100) against fair (35/100) for 6081-O.