Aluminum 6012-T4 vs 6012-T651
Aluminum · 6012 temper comparison
6012-T4 and 6012-T651 are two conditions of the same aluminum grade, 6012: T4 (solution heat treated and naturally aged) versus T651 (T6, stress relieved by stretching). The chemistry is identical, so every difference below comes from the condition. 6012-T651 is the stronger of the two: yield strength 295 MPa (42.8 ksi) against 150 MPa (21.8 ksi) for 6012-T4, about 97% more; tensile strength follows at 330 MPa (47.9 ksi) vs 255 MPa (37 ksi). In exchange, 6012-T4 is the more ductile: elongation 16% versus 10% for 6012-T651, and 6012-T651 is harder (100 HB vs 70 HB). 6012-T651 runs hotter in service (150°C vs 100°C continuous). On the shop floor, 6012-T651 machines more easily (96 vs 85 out of 100).
6012-T4Choose it when the part is bent, formed or impact-loaded.
6012-T651Choose it when strength drives the design, or when the part sees heat.
6012-T4 vs 6012-T651: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Fracture Toughness (K_IC) 26 MPa·√m23.7 ksi·√in · Hardness, Rockwell B 60 HRB
Physical
Density and transition temperatures.
Same in both: Density 2.72 g/cm³0.1 lb/in³ · Melting Point (Solidus) 580°C1,076 °F · Liquidus Temperature 650°C1,202 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 890 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.78 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 20 / 100 · Castability 35 / 100 · Brazeability / Solderability 25 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6012-T4 vs 6012-T651 — frequently asked
Is 6012-T651 stronger than 6012-T4?
Yes. 6012-T651 has a typical yield strength of 295 MPa (42.8 ksi) against 150 MPa (21.8 ksi) for 6012-T4 — about 97% more. Tensile strength is 330 MPa (47.9 ksi) vs 255 MPa (37 ksi).
Which condition does FabDigit quote by default, T4 or T651?
T6 is the default 6012 condition in the FabDigit quote flow (neither T4 nor T651). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6012-T4 or 6012-T651?
6012-T651, by a small margin. Both rate excellent for machinability — 96/100 against 85/100 for 6012-T4.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6012-T4 and 6012-T651 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.