Aluminum 6003-O vs 6003-T6
Aluminum · 6003 temper comparison
6003-O and 6003-T6 are two conditions of the same aluminum grade, 6003: O (annealed) versus T6 (solution heat treated and artificially aged). The chemistry is identical, so every difference below comes from the condition. 6003-T6 is the stronger of the two: yield strength 205 MPa (29.7 ksi) against 55 MPa (7.98 ksi) for 6003-O, about 3.7 times as much; tensile strength follows at 240 MPa (34.8 ksi) vs 115 MPa (16.7 ksi). In exchange, 6003-O is the more ductile: elongation 26% versus 10% for 6003-T6, and 6003-T6 is harder (75 HB vs 30 HB). 6003-O conducts heat better (195 W/m·K vs 175 W/m·K). On the shop floor, 6003-T6 machines more easily (fair vs poor).
6003-OChoose it when the part is bent, formed or impact-loaded.
6003-T6Choose it when strength drives the design, or when the part is machined in volume.
6003-O vs 6003-T6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Compressive Strength 205 MPa29.7 ksi · Fracture Toughness (K_IC) 29 MPa·√m26.4 ksi·√in · Hardness, Vickers 82 HV
Physical
Density and transition temperatures.
Same in both: Density 2.7 g/cm³0.1 lb/in³ · Melting Point (Solidus) 615°C1,139 °F · Liquidus Temperature 655°C1,211 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 897 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Max Service Temperature (continuous) 150°C302 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 3.83×10⁻⁸ Ω·m1.51 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.8 V · Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 35% · Weldability 80 / 100 · Castability 30 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
6003-O vs 6003-T6 — frequently asked
Is 6003-T6 stronger than 6003-O?
Yes. 6003-T6 has a typical yield strength of 205 MPa (29.7 ksi) against 55 MPa (7.98 ksi) for 6003-O — about 3.7 times as much. Tensile strength is 240 MPa (34.8 ksi) vs 115 MPa (16.7 ksi).
Which condition does FabDigit quote by default, O or T6?
T6 is the default 6003 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 6003-O or 6003-T6?
6003-T6. Its machinability rates fair (50/100) against poor (30/100) for 6003-O.