Aluminum 5A06-H112 vs 5A06-H14
Aluminum · 5A06 temper comparison
5A06-H112 and 5A06-H14 are two conditions of the same aluminum grade, 5A06: H112 (strain hardened from hot working only) versus H14 (strain hardened, half hard). The chemistry is identical, so every difference below comes from the condition. 5A06-H14 is the stronger of the two: yield strength 295 MPa (42.8 ksi) against 175 MPa (25.4 ksi) for 5A06-H112, about 69% more; tensile strength follows at 395 MPa (57.3 ksi) vs 340 MPa (49.3 ksi). In exchange, 5A06-H112 is the more ductile: elongation 16% versus 8% for 5A06-H14, and 5A06-H14 is harder (100 HB vs 75 HB).
5A06-H112Choose it when the part is bent, formed or impact-loaded.
5A06-H14Choose it when strength drives the design.
5A06-H112 vs 5A06-H14: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70 GPa10.2 Msi · Shear Modulus 26.4 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Compressive Strength 165 MPa23.9 ksi · Fracture Toughness (K_IC) 35 MPa·√m31.9 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 2.64 g/cm³0.1 lb/in³ · Melting Point (Solidus) 568°C1,054 °F · Liquidus Temperature 638°C1,180 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 920 J/kg·K0.22 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 24.7 µm/m·K13.7 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -253°C-423 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 26.5 % IACS · Electrical Resistivity 6.5×10⁻⁸ Ω·m2.56 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 40% · Brazeability / Solderability 20 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 210 MJ/kg90,284 BTU/lb · Embodied Carbon (primary production) 14 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5A06-H112 vs 5A06-H14 — frequently asked
Is 5A06-H14 stronger than 5A06-H112?
Yes. 5A06-H14 has a typical yield strength of 295 MPa (42.8 ksi) against 175 MPa (25.4 ksi) for 5A06-H112 — about 69% more. Tensile strength is 395 MPa (57.3 ksi) vs 340 MPa (49.3 ksi).
Which condition does FabDigit quote by default, H112 or H14?
O is the default 5A06 condition in the FabDigit quote flow (neither H112 nor H14). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5A06-H112 or 5A06-H14?
5A06-H14, by a small margin. Both rate fair for machinability — 52/100 against 45/100 for 5A06-H112.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5A06-H112 and 5A06-H14 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.