Aluminum 5654-H34 vs 5654-O
Aluminum · 5654 temper comparison
5654-H34 and 5654-O are two conditions of the same aluminum grade, 5654: H34 (strain hardened and stabilized, half hard) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. 5654-H34 is the stronger of the two: yield strength 230 MPa (33.4 ksi) against 115 MPa (16.7 ksi) for 5654-O, about 100% more; tensile strength follows at 290 MPa (42.1 ksi) vs 240 MPa (34.8 ksi). In exchange, 5654-O is the more ductile: elongation 25% versus 13% for 5654-H34, and 5654-H34 is harder (73 HB vs 58 HB). On the shop floor, 5654-H34 machines more easily (46 vs 35 out of 100).
5654-H34Choose it when strength drives the design, or when the part is machined in volume.
5654-OChoose it when the part is bent, formed or impact-loaded.
5654-H34 vs 5654-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 70.3 GPa10.2 Msi · Shear Modulus 26.4 GPa3.8 Msi · Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33 · Hardness, Rockwell B 25 HRB
Physical
Density and transition temperatures.
Same in both: Density 2.66 g/cm³0.1 lb/in³ · Melting Point (Solidus) 593°C1,099 °F · Liquidus Temperature 643°C1,189 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.9 µm/m·K13.3 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 65°C149 °F · Min Service Temperature -270°C-454 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.4×10⁻⁸ Ω·m2.13 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V · Corrosion Resistance 87 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 30% · Weldability 92 / 100 · Brazeability / Solderability 20 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 20%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5654-H34 vs 5654-O — frequently asked
Is 5654-H34 stronger than 5654-O?
Yes. 5654-H34 has a typical yield strength of 230 MPa (33.4 ksi) against 115 MPa (16.7 ksi) for 5654-O — about 100% more. Tensile strength is 290 MPa (42.1 ksi) vs 240 MPa (34.8 ksi).
Which condition does FabDigit quote by default, H34 or O?
O is the default 5654 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5654-H34 or 5654-O?
5654-H34, by a small margin. Both rate fair for machinability — 46/100 against 35/100 for 5654-O.