Aluminum 5183-H111 vs 5183-O
Aluminum · 5183 temper comparison
5183-H111 and 5183-O are two conditions of the same aluminum grade, 5183: H111 (slightly strain hardened) versus O (annealed). The chemistry is identical, so every difference below comes from the condition. 5183-H111 is the stronger of the two: yield strength 150 MPa (21.8 ksi) against 130 MPa (18.9 ksi) for 5183-O, about 15% more; tensile strength follows at 300 MPa (43.5 ksi) vs 285 MPa (41.3 ksi). In exchange, 5183-O is the more ductile: elongation 24% versus 18% for 5183-H111, and 5183-H111 is harder (82 HB vs 75 HB).
5183-H111Choose it when strength drives the design.
5183-OChoose it when the part is bent, formed or impact-loaded.
5183-H111 vs 5183-O: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 71 GPa10.3 Msi · Shear Modulus 26.4 GPa3.8 Msi · Bulk Modulus 70 GPa10.2 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Same in both: Density 2.66 g/cm³0.1 lb/in³ · Melting Point (Solidus) 574°C1,065 °F · Liquidus Temperature 638°C1,180 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Max Service Temperature (continuous) 65°C149 °F · Min Service Temperature -270°C-454 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.87 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 95 / 100 · Castability 25 / 100 · Brazeability / Solderability 15 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5183-H111 vs 5183-O — frequently asked
Is 5183-H111 stronger than 5183-O?
Yes. 5183-H111 has a typical yield strength of 150 MPa (21.8 ksi) against 130 MPa (18.9 ksi) for 5183-O — about 15% more. Tensile strength is 300 MPa (43.5 ksi) vs 285 MPa (41.3 ksi).
Which condition does FabDigit quote by default, H111 or O?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, 5183-H111 or 5183-O?
5183-H111, by a small margin. Both rate fair for machinability — 52/100 against 45/100 for 5183-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5183-H111 and 5183-O side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.