Aluminum 2A16-O vs 2A16-T4
Aluminum · 2A16 temper comparison
2A16-O and 2A16-T4 are two conditions of the same aluminum grade, 2A16: O (annealed) versus T4 (solution heat treated and naturally aged). The chemistry is identical, so every difference below comes from the condition. 2A16-T4 is the stronger of the two: yield strength 185 MPa (26.8 ksi) against 80 MPa (11.6 ksi) for 2A16-O, about 131% more; tensile strength follows at 340 MPa (49.3 ksi) vs 185 MPa (26.8 ksi). In exchange, 2A16-O is the more ductile: elongation 20% versus 16% for 2A16-T4, and 2A16-T4 is harder (90 HB vs 48 HB). 2A16-O runs hotter in service (200°C vs 150°C continuous) and 2A16-O conducts heat better (170 W/m·K vs 120 W/m·K). On the shop floor, 2A16-T4 machines more easily (good vs fair).
2A16-OChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
2A16-T4Choose it when strength drives the design, or when the part is machined in volume.
2A16-O vs 2A16-T4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 76 GPa11 Msi · Poisson's Ratio 0.33 · Compressive Strength 275 MPa39.9 ksi · Fracture Toughness (K_IC) 30 MPa·√m27.3 ksi·√in · Hardness, Vickers 118 HV
Physical
Density and transition temperatures.
Same in both: Density 2.84 g/cm³0.1 lb/in³ · Melting Point (Solidus) 540°C1,004 °F · Liquidus Temperature 645°C1,193 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 864 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 22.6 µm/m·K12.6 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 5.75×10⁻⁸ Ω·m2.26 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.66 V · Corrosion Resistance 33 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 200% · Weldability 72 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 210 MJ/kg90,284 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,150 L/kg138 gal/lb · Typical Recycled Content 8%
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
2A16-O vs 2A16-T4 — frequently asked
Is 2A16-T4 stronger than 2A16-O?
Yes. 2A16-T4 has a typical yield strength of 185 MPa (26.8 ksi) against 80 MPa (11.6 ksi) for 2A16-O — about 131% more. Tensile strength is 340 MPa (49.3 ksi) vs 185 MPa (26.8 ksi).
Which condition does FabDigit quote by default, O or T4?
T6 is the default 2A16 condition in the FabDigit quote flow (neither O nor T4). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 2A16-O or 2A16-T4?
2A16-T4. Its machinability rates good (62/100) against fair (45/100) for 2A16-O.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2A16-O and 2A16-T4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.