Benchmark · 4 materials
Aluminum 6082 vs Aluminum 2007 vs Aluminum 2017 vs Aluminum 2017A
All aluminum grades — bands show the family's 10th–90th percentile. The best value in each row is in bold; metric first, imperial in gray.
Properties
| Property | 6082 | 2007 | 2017 | 2017A |
|---|---|---|---|---|
| Yield strengthMPa | 255 MPa37 ksi | 250 MPa36 ksi | 275 MPa40 ksi | 275 MPa40 ksi |
| Tensile strengthMPa | 290 MPa42 ksi | 320 MPa46 ksi | 425 MPa62 ksi | 425 MPa62 ksi |
| Specific strengthMPa·cm³/g | 94 | 88 | 99 | 99 |
| Densityg/cm³ | 2.71 g/cm³0.098 lb/in³ | 2.84 g/cm³0.103 lb/in³ | 2.79 g/cm³0.101 lb/in³ | 2.79 g/cm³0.101 lb/in³ |
| Hardness (HB equiv.)HB | 95 HB | 95 HB | 105 HB | 105 HB |
| Max service temp°C | 150 °C302 °F | 150 °C302 °F | 150 °C302 °F | 150 °C302 °F |
| Min service temp°C | -200 °C-328 °F | -200 °C-328 °F | -200 °C-328 °F | -200 °C-328 °F |
| Electrical conductivity% IACS | 47 % IACS27.3 MS/m | 31 % IACS18 MS/m | 33 % IACS19.1 MS/m | 33 % IACS19.1 MS/m |
| Machinability/100 | Very good70 / 100 | Excellent95 / 100 | Excellent90 / 100 | Excellent85 / 100 |
| Weldability/100 | Very good80 / 100 | Not recommended10 / 100 | Not recommended10 / 100 | Not recommended10 / 100 |
| Formability/100 | Fair50 / 100 | Poor25 / 100 | Poor30 / 100 | Poor30 / 100 |
| Relative cost | $$ Standard | $$$ Premium | $$$ Premium | $$$ Premium |
| Processes | CNC, Sheet | CNC, Sheet | CNC, Sheet | CNC, Sheet |
Where each grade sits
One track per property; coloured markers are the compared grades, the shaded band is the aluminum family 10th–90th percentile and the tick its median.
Yield strength255 MPa
50 MPafamily median 175 MPa468 MPa
Tensile strength290 MPa
110 MPafamily median 290 MPa525 MPa
Density2.71 g/cm³
2.66 g/cm³family median 2.71 g/cm³2.82 g/cm³
Hardness (HB equiv.)95 HB
28 HBfamily median 78 HB145 HB
Max service temp150 °C
100 °Cfamily median 150 °C200 °C
Electrical conductivity47 % IACS
29 % IACSfamily median 38 % IACS52 % IACS
Machinability70 / 100
45 / 100family median 60 / 10085 / 100
Relative cost22
16family median 2248
6082200720172017A
Strength versus weight
Manufacturing and finishing
| Capability | 6082 | 2007 | 2017 | 2017A |
|---|---|---|---|---|
| CNC machining | Yes | Yes | Yes | Yes |
| Sheet metal | Yes | Yes | Yes | Yes |
| Default condition | — | — | — | — |
| Min. machined wall | 0.5 mm | 0.5 mm | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm | Ra 0.8 µm | Ra 0.8 µm |
| Heat treatments | Age T6 (Aluminum), Age T651 (Aluminum), Full Anneal | Age T6 (Aluminum), Age T651 (Aluminum), Full Anneal | Age T6 (Aluminum), Age T651 (Aluminum), Full Anneal | Age T6 (Aluminum), Age T651 (Aluminum), Full Anneal |
| Anodizing Type II | Yes | Yes | Yes | Yes |
| Cerakote | Yes | Yes | Yes | Yes |
| Chem Film (Alodine) | Yes | Yes | Yes | Yes |
| Chemical Etching | Yes | Yes | Yes | Yes |
| DLC | Yes | Yes | Yes | Yes |
| Dot Peen Marking | Yes | Yes | Yes | Yes |
| E-Coating | Yes | Yes | Yes | Yes |
| Electro-chemical Etching | Yes | Yes | Yes | Yes |
| Electroless Nickel (EN) | Yes | Yes | Yes | Yes |
| Electropolishing | Yes | Yes | Yes | Yes |
| Embossing / Debossing | Yes | Yes | Yes | Yes |
| Epoxy Coating | Yes | Yes | Yes | Yes |
| Gold Plating | Yes | Yes | Yes | Yes |
| Hard Anodize Type III w/ PTFE | Yes | Yes | Yes | Yes |
| Hard Anodizing Type III | Yes | Yes | Yes | Yes |
| Ink Stamping | Yes | Yes | Yes | Yes |
| Laser Marking | Yes | Yes | Yes | Yes |
| Mechanical Engraving | Yes | Yes | Yes | Yes |
Showing 18 of 25 finishes — the full list is on each grade's datasheet.
Typical handbook values for the default condition, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.