Steel 9310 vs P20
Steel · grade comparison
Steel 9310 and P20 are both steel grades. 9310 is the stronger of the two: yield strength 600 MPa (87 ksi) against 440 MPa (63.8 ksi) for P20, about 36% more; tensile strength follows at 950 MPa (138 ksi) vs 700 MPa (102 ksi). In exchange, P20 is the more ductile: elongation 20% versus 15% for 9310, and 9310 is harder (270 HB vs 200 HB). P20 runs hotter in service (450°C vs 400°C continuous). On the shop floor, P20 machines more easily (good vs fair), P20 welds better (50 vs 38 out of 100), and 9310 sits in a lower cost tier (premium, $$$) than P20 (specialty, $$$$$).
9310Choose it when strength drives the design, or when cost is the deciding factor.
P20Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
9310 vs P20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 60 L/kg7.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 9310 | P20 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | HR | Annealed |
| Relative cost | $$$ Premium | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
9310 vs P20 — frequently asked
Is 9310 stronger than P20?
Yes. 9310 has a typical yield strength of 600 MPa (87 ksi) against 440 MPa (63.8 ksi) for P20 — about 36% more. Tensile strength is 950 MPa (138 ksi) vs 700 MPa (102 ksi).
Which is cheaper, 9310 or P20?
9310 is the lower-cost material: it sits in the premium tier ($$$) while P20 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 9310 or P20?
P20. Its machinability rates good (65/100) against fair (40/100) for 9310; for welding the order is P20 first (fair, 50/100) then 9310 (fair, 38/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 9310 and P20 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.