PI 15% Graphite + 10% PTFE vs PI CF30
Polymer · PI grade comparison
PI 15% Graphite + 10% PTFE and PI CF30 are two grades of the same polymer grade, PI: 15% Graphite + 10% PTFE versus CF30 (30% carbon-fiber reinforced polyimide). The chemistry is identical, so every difference below comes from the condition. PI CF30 is the stronger of the two: tensile strength 100 MPa (14.5 ksi) against 44 MPa (6.38 ksi) for PI 15% Graphite + 10% PTFE, about 127% more. In exchange, PI 15% Graphite + 10% PTFE is the more ductile: elongation 3.5% versus 2% for PI CF30. PI CF30 is lighter (1.45 g/cm³ vs 1.55 g/cm³ for PI 15% Graphite + 10% PTFE) and PI CF30 is stiffer (12 GPa vs 3.4 GPa). On the shop floor, PI 15% Graphite + 10% PTFE machines more easily (good vs fair).
PI 15% Graphite + 10% PTFEChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
PI CF30Choose it when strength drives the design, or when weight is the constraint.
PI 15% Graphite + 10% PTFE vs PI CF30: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
PI 15% Graphite + 10% PTFEPI CF30
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Same in both: Shear Modulus 1.1 GPa0.16 Msi · Bulk Modulus 6 GPa0.8 Msi · Poisson's Ratio 0.41 · Compressive Modulus 2.9 GPa0.42 Msi
Physical
Density and transition temperatures.
Density
Same in both: Glass Transition (Tg) 385°C725 °F · Water Absorption (24 h) 0.3% · Water Absorption (Saturation) 1.2% · Refractive Index 1.7
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,130 J/kg·K0.27 BTU/lb·°F · Min Service Temperature -240°C-400 °F · Heat Deflection Temp. @ 0.45 MPa 400°C752 °F · Max Service Temperature (short-term) 480°C896 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Dielectric Strength 22 kV/mm559 V/mil · Dielectric Constant (1 MHz) 3.5 · Dissipation Factor (1 MHz) 0.0034 · Volume Resistivity 1×10¹⁶ Ω·cm · Surface Resistivity 1×10¹⁵ Ω
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: UV / Weathering Resistance 60 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Weldability 5 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 290 MJ/kg124,678 BTU/lb · Embodied Carbon (primary production) 13 kg CO₂/kg · Embodied Water 600 L/kg71.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PI 15% Graphite + 10% PTFE vs PI CF30 — frequently asked
Is PI CF30 stronger than PI 15% Graphite + 10% PTFE?
Yes. PI CF30 has a typical tensile strength of 100 MPa (14.5 ksi) against 44 MPa (6.38 ksi) for PI 15% Graphite + 10% PTFE — about 127% more.
Which grade does FabDigit quote by default, 15% Graphite + 10% PTFE or CF30?
Specify the condition in the material field or the drawing note; FabDigit prices the quote for the state you call out.
Which is easier to machine, PI 15% Graphite + 10% PTFE or PI CF30?
PI 15% Graphite + 10% PTFE. Its machinability rates good (62/100) against fair (35/100) for PI CF30.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PI 15% Graphite + 10% PTFE and PI CF30 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.