Copper Alloy C82600 vs Cu-ETP1
Copper Alloy · grade comparison
Copper Alloy C82600 and Cu-ETP1 are both copper alloy grades. C82600 is the stronger of the two: yield strength 1,035 MPa (150 ksi) against 70 MPa (10.2 ksi) for Cu-ETP1, about 15 times as much; tensile strength follows at 1,140 MPa (165 ksi) vs 220 MPa (31.9 ksi). In exchange, Cu-ETP1 is the more ductile: elongation 40% versus 1% for C82600, and C82600 is harder (400 HB vs 45 HB). C82600 is lighter (8.23 g/cm³ vs 8.93 g/cm³ for Cu-ETP1) and C82600 is stiffer (131 GPa vs 117 GPa). On the shop floor, C82600 machines more easily (fair vs poor) and Cu-ETP1 welds better (fair vs poor).
C82600Choose it when strength drives the design, or when weight is the constraint.
Cu-ETP1Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
C82600 vs Cu-ETP1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Latent Heat of Fusion
Same in both: Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.25 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C82600 | Cu-ETP1 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C82600 vs Cu-ETP1 — frequently asked
Is C82600 stronger than Cu-ETP1?
Yes. C82600 has a typical yield strength of 1,035 MPa (150 ksi) against 70 MPa (10.2 ksi) for Cu-ETP1 — about 15 times as much. Tensile strength is 1,140 MPa (165 ksi) vs 220 MPa (31.9 ksi).
Which is cheaper, C82600 or Cu-ETP1?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C82600 or Cu-ETP1?
C82600. Its machinability rates fair (45/100) against poor (30/100) for Cu-ETP1; for welding the order is Cu-ETP1 first (fair, 50/100) then C82600 (poor, 30/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C82600 and Cu-ETP1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.