Copper Alloy C10400-H01 vs C10400-H03
Copper Alloy · C10400 temper comparison
C10400-H01 and C10400-H03 are two conditions of the same copper alloy grade, C10400: H01 (quarter hard) versus H03 (three-quarter hard). The chemistry is identical, so every difference below comes from the condition. C10400-H03 is the stronger of the two: yield strength 280 MPa (40.6 ksi) against 205 MPa (29.7 ksi) for C10400-H01, about 37% more; tensile strength follows at 315 MPa (45.7 ksi) vs 262 MPa (38 ksi). In exchange, C10400-H01 is the more ductile: elongation 25% versus 10% for C10400-H03, and C10400-H03 is harder (88 HB vs 70 HB).
C10400-H01Choose it when the part is bent, formed or impact-loaded.
C10400-H03Choose it when strength drives the design.
C10400-H01 vs C10400-H03: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 117 GPa17 Msi · Shear Modulus 44 GPa6.4 Msi · Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Reduction in Area 60%
Physical
Density and transition temperatures.
Same in both: Density 8.94 g/cm³0.32 lb/in³ · Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 17 µm/m·K9.4 µin/in·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb · Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 100 % IACS · Electrical Resistivity 1.72×10⁻⁸ Ω·m0.677 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.22 V · Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Weldability 65 / 100 · Castability 45 / 100 · Brazeability / Solderability 95 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 57 MJ/kg24,506 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 250 L/kg30 gal/lb · Typical Recycled Content 10%
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C10400-H01 vs C10400-H03 — frequently asked
Is C10400-H03 stronger than C10400-H01?
Yes. C10400-H03 has a typical yield strength of 280 MPa (40.6 ksi) against 205 MPa (29.7 ksi) for C10400-H01 — about 37% more. Tensile strength is 315 MPa (45.7 ksi) vs 262 MPa (38 ksi).
Which condition does FabDigit quote by default, H01 or H03?
H04 is the default C10400 condition in the FabDigit quote flow (neither H01 nor H03). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C10400-H01 or C10400-H03?
C10400-H03, by a small margin. Both rate poor for machinability — 30/100 against 24/100 for C10400-H01.