Hardboard vs LVL
Natural Material · grade comparison
Hardboard and LVL are both natural material grades. LVL is the stronger of the two: tensile strength 42 MPa (6.09 ksi) against 20 MPa (2.9 ksi) for Hardboard, about 110% more. In exchange, Hardboard is the more ductile: elongation 1% versus 0.8% for LVL. LVL is lighter (0.55 g/cm³ vs 0.95 g/cm³ for Hardboard) and LVL is stiffer (13.8 GPa vs 4.2 GPa). On the shop floor, LVL machines more easily (excellent vs very good).
HardboardChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
LVLChoose it when strength drives the design, or when weight is the constraint.
Hardboard vs LVL: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Same in both: Shear Strength 7 MPa0.94 ksi
Physical
Density and transition temperatures.
Density
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every natural material grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Hardboard | LVL |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Hardboard vs LVL — frequently asked
Is LVL stronger than Hardboard?
Yes. LVL has a typical tensile strength of 42 MPa (6.09 ksi) against 20 MPa (2.9 ksi) for Hardboard — about 110% more.
Which is cheaper, Hardboard or LVL?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Hardboard or LVL?
LVL. Its machinability rates excellent (85/100) against very good (70/100) for Hardboard.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hardboard and LVL side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.