Copper Alloy Cu-ETP1 vs CuAg0.07(OF)
Copper Alloy · grade comparison
Copper Alloy Cu-ETP1 and CuAg0.07(OF) are both copper alloy grades. Both yield at about 70 MPa — strength does not separate them. CuAg0.07(OF) is the more ductile: elongation 45% versus 40% for Cu-ETP1, and CuAg0.07(OF) is harder (55 HV vs 50 HV). CuAg0.07(OF) runs hotter in service (300°C vs 200°C continuous). On the shop floor, CuAg0.07(OF) welds better (good vs fair).
CuAg0.07(OF)Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
Cu-ETP1 vs CuAg0.07(OF): propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34 · Yield Strength (0.2% offset) 70 MPa10.2 ksi · Shear Strength 150 MPa21.8 ksi · Hardness, Brinell 45 HB
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Castability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Strength (UTS / density) 25 kN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Cu-ETP1 | CuAg0.07(OF) |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
Cu-ETP1 vs CuAg0.07(OF) — frequently asked
What is the difference between Cu-ETP1 and CuAg0.07(OF)?
Copper Alloy Cu-ETP1 and CuAg0.07(OF) are both copper alloy grades. Both yield at about 70 MPa — strength does not separate them. CuAg0.07(OF) is the more ductile: elongation 45% versus 40% for Cu-ETP1, and CuAg0.07(OF) is harder (55 HV vs 50 HV).
Which is cheaper, Cu-ETP1 or CuAg0.07(OF)?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Cu-ETP1 or CuAg0.07(OF)?
Cu-ETP1, by a small margin. Both rate poor for machinability — 30/100 against 22/100 for CuAg0.07(OF); for welding the order is CuAg0.07(OF) first (good, 60/100) then Cu-ETP1 (fair, 50/100).