Copper Alloy Cu-ETP1 vs CuAg0.04
Copper Alloy · grade comparison
Copper Alloy Cu-ETP1 and CuAg0.04 are both copper alloy grades. CuAg0.04 is the stronger of the two: yield strength 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for Cu-ETP1, about 4.4 times as much; tensile strength follows at 360 MPa (52.2 ksi) vs 220 MPa (31.9 ksi). In exchange, Cu-ETP1 is the more ductile: elongation 40% versus 8% for CuAg0.04, and CuAg0.04 is harder (105 HB vs 45 HB). CuAg0.04 is stiffer (125 GPa vs 117 GPa) and CuAg0.04 runs hotter in service (220°C vs 200°C continuous). On the shop floor, Cu-ETP1 welds better (50 vs 35 out of 100).
Cu-ETP1Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
CuAg0.04Choose it when strength drives the design, or when the part sees heat.
Cu-ETP1 vs CuAg0.04: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Hardness, Rockwell B
Same in both: Bulk Modulus 140 GPa20.3 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 1,065°C1,949 °F · Liquidus Temperature 1,083°C1,981 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 385 J/kg·K0.09 BTU/lb·°F · Latent Heat of Fusion 205 J/g88.1 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 65 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Castability 45 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Cu-ETP1 | CuAg0.04 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
Cu-ETP1 vs CuAg0.04 — frequently asked
Is CuAg0.04 stronger than Cu-ETP1?
Yes. CuAg0.04 has a typical yield strength of 310 MPa (45 ksi) against 70 MPa (10.2 ksi) for Cu-ETP1 — about 4.4 times as much. Tensile strength is 360 MPa (52.2 ksi) vs 220 MPa (31.9 ksi).
Which is cheaper, Cu-ETP1 or CuAg0.04?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, Cu-ETP1 or CuAg0.04?
Cu-ETP1. Its weldability rates fair (50/100) against fair (35/100) for CuAg0.04.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Cu-ETP1 and CuAg0.04 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.